文章信息/Info

Title:
Research on preparation of high purity ferrous oxalate
from desulphurization slag with high iron
文章编号:
16742869(2010)07006203
作者:
张莉1; 丁瑶2; 刁杰1; 彭峰莉1
1.武汉工程大学环境与城市建设学院，湖北 武汉430074；
2.武汉工程大学化工与制药学院，湖北 武汉 430074
Author(s):
ZHANG Li1;  DING Yao2;  DIAO Jie1; PENG Fengli1
1.School of Environment and Civil Engineering，Wuhan Institute of Technology，Wuhan 430074， China；
2. School of Chemical Engineering and Pharmacy, Wuhan Instictute of Technology, Wuhan 430074, China
关键词:
高铁脱硫渣; 硫酸亚铁; 草酸亚铁; 粒径
Keywords:
 ; highiron desulfurization slag; ferrous sulfate; ferrous oxalate; the particle size
分类号:
TQ138.11
DOI:
10.3969/j.issn.16742869.2010.07.016
文献标志码:
A
摘要:
以高铁脱硫渣为原料，采取酸浸、还原反应、离心分离、结晶、合成反应、过滤、干燥等工艺制备出99%以上草酸亚铁晶体.研究了反映剂量、反应温度、加料时间对草酸亚铁纯度的影响，讨论了每个因素的规律性.结果表明：14 g硫酸亚铁溶于15 mL水中，用6 mL氨水预处理，6.5 g草酸溶于25 mL水中，用40 mL无水乙醇预处理，反应温度在40 ℃，加料时间在25～30 min，得到纯度为99％以上、平均粒径为5.0 μm的高纯度超细草酸亚铁.
Abstract:
Using desulfurization slag with high iron as raw material, ferrous oxalate with purity has been made over 99％ by acid leaching，reduction reaction，centrifugal separation，purifying，crystallizing，synthesis reaction，filtration and drying. The effects of the dose， temperature and feeding time on the purity of ferrous oxalate were studied，and the regularity of these affecting factors was discussed. The results showed that appropriate leaching conditions are as follows：14 g ferrous sulfate dissolved in 15 mL water, with 6 mL ammonia pretreatment， 6.5 g oxalic acid dissolved in 25 mL water with 40 mL ethanol pretreatment. And then under 40 ℃ and feeding time 25-30 min，we got ferrous oxalate powder with purity of 99.1 %， and average particle size of 5.0 μm.

参考文献/References:

［1］张婕，丛玉伟，王淑华.铁水脱硫用聚渣剂的研制［J］，山东冶金，2005,27(2):12.
［2］郭兴忠，李劲明，文光远,等.攀钢脱硫前后罐渣改性的实验［J］，钢铁钒钛，2001,22(4): 12.
［3］Waterman H C，Vivian D L．Direct ringclosure through a nitro group in certain aromatic compounds   with the formation of nitrogen heterocycles：a new reaction［J］．J Organ Chemistry，1949，14：289297．
［4］张莉，彭峰莉，毛静,等.高铁脱硫渣制备高纯度硫酸亚铁及草酸亚铁的研究［J］.环境工程学报，2009,3(6):14.
［5］彭爱国,贺周初,余长艳,等.高纯超细草酸亚铁的制备研究［J］.精细化工中间体，2008,38(4):2.

相似文献/References:

[1]关洪亮,操艳兰,顾逸雅,等.硫酸亚铁沉淀法处理含钒废水[J].武汉工程大学学报,2012,(12):25.[doi:103969/jissn16742869201212007]
　GUAN Hong liang,CAO Yan lan,GU Yi ya,et al.Precipitating treatment of vanadium contained waste water by using ferrous sulfate[J].Journal of Wuhan Institute of Technology,2012,(07):25.[doi:103969/jissn16742869201212007]
[2]彭爱国,贺周初,余长艳,等.电池级超微细磷酸铁的制备[J].武汉工程大学学报,2013,(07):1.[doi:103969/jissn16742869201307001]
　PENG Ai guo,HE Zhou chu,YU Chang yan,et al.Preparation of batterygrade ultra fine iron phosphates[J].Journal of Wuhan Institute of Technology,2013,(07):1.[doi:103969/jissn16742869201307001]

备注/Memo

备注/Memo:
收稿日期：20100408作者简介：张莉(1965)，女，湖北武汉人，副教授，硕士.研究方向：水污染控制工程以及清洁生产.
更新日期/Last Update: