|本期目录/Table of Contents|

[1]段颖姗,陈云,王营茹,等.羟基铁交联累托石电化学处理苯酚废水[J].武汉工程大学学报,2012,(4):35-38.
　DUAN Ying\|shan,CHEN Yun,WANG Ying\|ru,et al.Electrochemical treating phenol wastewater with hydroxy\|ferrum cross\|linked rectorite[J].Journal of Wuhan Institute of Technology,2012,(4):35-38.
点击复制

羟基铁交联累托石电化学处理苯酚废水(/HTML)
分享到：

《武汉工程大学学报》[ISSN:1674-2869/CN:42-1779/TQ]

卷:
期数:
2012年4期
页码:
35-38
栏目:
资源与土木工程
出版日期:
2012-05-30

文章信息/Info

Title:
Electrochemical treating phenol wastewater
 with hydroxy\|ferrum cross\|linked rectorite
文章编号:
16742869(2012)04003504
作者:
段颖姗1; 2; 陈云1; 王营茹1; 黄升谋2*; 冯文瑄1; 陈金毅1; 孙家寿1
1.武汉工程大学环境与城市建设学院，湖北 武汉430074；
2.襄樊学院化学工程与食品科学学院，湖北 襄阳441053
Author(s):
DUAN Ying\|shan1; 2;  CHEN Yun1;  WANG Ying\|ru1;  HUANG Sheng\|mou2;  FENG Wen\|xuan1;  CHEN Jin\|yi1;  SUN Jia\|shou1
1.School of Environmental and Civil Engineering， Wuhan Institute of Technology, Wuhan 430074，China;
2.College of Chemical Engineering and Food Science，Xiangfan University, Xiangyang 441053, China
关键词:
羟基铁; 交联累托石; 电化学; 苯酚
Keywords:
hydroxy\|ferrum;  cross\|linked rectorite;  electrochemical;  phenol
分类号:
X703
DOI:
-
文献标志码:
AAdoi:103969/jissn16742869201204009
摘要:
利用三氯化铁制备羟基铁交联剂，当pH值为5，FeCl3·6H2O固体投加量为10 mmol/g累托石，液固比为5∶1，反应时间为4 h，反应温度为60 ℃时，成功制备了改性累托石复合材料.利用制备的羟基铁交联累托石复合材料电化学处理含苯酚废水，结果表明：当电压为6 V，电解质NaCl浓度为0.1 mol/L，苯酚pH值为4，苯酚质量浓度为200 mg/L时，该复合材料能够很好地催化降解苯酚废水，其降解率可达到95%以上.
Abstract:
Hydroxy\|ferrum prepared by ferric chloride as the cross\|linking agent, the modified rectorite composite was prepared successfully when the optimum reaction conditions were as follows: the pH 5, the addition of ferric chloride 10 mmol/grectorite, the liquid\|solid ratio 5∶1, the reaction time 4 h, the temperature 60 ℃.Then the phenol wastewater was degradated by electrochemical method with modified rectorite composite. The results indicate that modified rectorite composite shows good function on the treatment of phenol waste water and the degradation rate reaches over 95% when voltage is 6 V, NaCl electrolyte solution is 0.1  mol/L, pH of phenol is 4, initial mass concentration of simulate phenol waste water is 200 mg/L.

参考文献/References:

［1］江涛，刘源骏.累托石［M］.武汉：湖北科学技术出版社，1989，40\|49.
［2］孙冬兰.累托石的钛层柱合成［J］.离子交换与吸附，1996，12(6): 542\|550.
［3］孙家寿，张泽强，刘羽，等.累托石层孔材料处理含铬废水的研究［J］.岩石矿物学，2001(4): 555\|558.
［4］孙家寿，石眺霞，张立娟.累托石层孔材料处理制药废水研究［J］.非金属矿，2004，27(3): 40\|42.
［5］孙家寿，张泽强，沈静，等.累托石层孔材料在废水处理中的应用研究（Ⅲ）——含硝基苯废水处理［J］.武汉化工学院学报，2004，25(1):43\|45.
［6］孙家寿，鲍世聪，李春领，等. 层柱累托石处理含氰废水研究［J］.非金属矿，2001(1):34\|37.
［7］孙家寿,石眺霞,张蕾，等.Ti/Fe层柱累托石电催化降解硝基苯废水的研究［J］.武汉工程大学学报，2007，29（3）：30\|34.
［8］孙家寿,张蕾,陈伟亚，等.固定化生物累托石处理分散生活污水的研究(Ⅳ)——固定化生物累托石处理生活废水的反应动力学［J］.武汉工程大学学报，2009，31（3）：49\|51.
［9］孙家寿,张蕾,陈伟亚，等.生物累托石处理生活污水试验研究［J］.环保科技，2010，16（1）:1\|6.
［10］孙家寿，陈金毅，陈茂荣，等. 层柱累托石复合材料的制备及表征［J］.中国非金属矿工业导报，2010（1）：22\|26.
［11］孙家寿,秦海燕,张立娟，等.累托石层孔材料在废水处理中的应用(IX)［J］.武汉工程大学学报，2007，29(1): 29\|31.
［12］国家环境保护总局《水和废水监测分析方法》编委会.水和废水监测分析方法［M］.4版.北京：中国环境出版社，2003.
［13］尹娟娟，袁凤英，宋伟冬，等.高级氧化技术处理苯酚废水的研究［J］.工业安全与环保，2008，34(10)：11\|12.

相似文献/References:

备注/Memo

备注/Memo:
-
更新日期/Last Update: