|本期目录/Table of Contents|

[1]周爱军,彭旭,付艳梅,等.吸水吸油双功能树脂的制备与表征[J].武汉工程大学学报,2012,(8):58-61.[doi:103969/jissn16742869201208015]
　ZHOU Ai jun,PENG Xu,FU Yan mei,et al.Preparation and characterization of bifunctional resin with water and oil absorption[J].Journal of Wuhan Institute of Technology,2012,(8):58-61.[doi:103969/jissn16742869201208015]
点击复制

吸水吸油双功能树脂的制备与表征(/HTML)
分享到：

《武汉工程大学学报》[ISSN:1674-2869/CN:42-1779/TQ]

卷:
期数:
2012年8期
页码:
58-61
栏目:
资源与土木工程
出版日期:
2012-09-10

文章信息/Info

Title:
Preparation and characterization of bifunctional resin with
water and oil absorption
文章编号:
16742869(2012)08005804
作者:
周爱军1; 彭旭1; 付艳梅1; 钟毅1; 周厚仁1; 叶海艮2
1武汉工程大学材料科学与工程学院，湖北 武汉 430074；
2中南橡胶集团有限责任公司，湖北 宜昌 443000
Author(s):
ZHOU Aijun1;  PENG Xu1;  FU Yanmei1;  ZHONG Yi1;  ZHOU Houren1;  YE Hangen2
1.School of Materials Science and Engineering, Wuhan Institute of Technology, Wuhan 430074, China；
2.Zhongnan Rubber Group Co.Ltd. Yichang 443000, China
关键词:
双功能树脂; 吸水吸油; 复合引发交联体系
Keywords:
bifunctional resin;  water and oil absorption;  combined initiation and crosslinking system
分类号:
TQ 325.7
DOI:
103969/jissn16742869201208015
文献标志码:
A
摘要:
以可溶性淀粉和甲基丙烯酸丁酯(MBA)为单体，硝酸铈(主要作用离子为Ce4+) 和偶氮二异丁腈(AIBN)为复合引发剂，N,N-亚甲基双丙烯酰胺(BIS)和二乙烯基苯(DVB)为复合交联剂，制备出吸水吸油双功能树脂.结果表明：当可溶性淀粉和MBA的质量配比为3∶2，Ce4+与AIBN的质量配比为1∶1，BIS和DVB的质量配比为1∶1时，制备的双功能树脂的吸水吸油达到最大值，分别为6 g/g和5.5 g/g.红外光谱和热失重分析表征显示单体进行了很好的交联，聚合物的热稳定性良好.
Abstract:
Bifunctional resin with water and oil absorption was prepared by using soluble starch and butyl methacrylate (MBA) as monomers, cerium nitrate(Ce4+) and azobisisobutyronitrile (AIBN) as combined initiators, N, Nmethylene acrylamide (BIS) and divinylbenzene (DVB)as crosslinking agents. The results show that the optimum monomer ratio, initiators ratio and crosslinking ratio values were∶m(soluble starch)∶m(MBA) = 3∶2; m(Ce4+)∶m(AIBN) = 1∶1; m(BIS)∶m(DVB) = 1∶1. At this point, the water and oil absorption rates of bifunctional resin reach their maximum of 6g/g and 5.5g/g. The monomers are well crosslinked and the thermal stability of the polymer is excellent by using infrared spectrograph and thermogravimetry to characterize the structure and thermal stability of the bifunctional resin.

参考文献/References:

［1］王筠.两亲性聚合物的合成与性能研究\[D\].合肥：中国科学技术大学，2010.
［2］童小丽, 吴璧耀. 两亲性超支化树脂的合成及其对钛白粉分散性的影响\[J\]. 武汉工程大学学报，2011(5)：7477.
［3］D R 保罗，C B 巴克纳尔．聚合物共混物：组成与性能上卷\[M\]．北京：科学出版社，2003．
［4］徐祖顺, 易昌凤. 两亲聚合物溶液性质及其乳液聚合的研究进展\[J\]. 高分子材料科学与工程, 1998, 14(4): 14.
［5］Khalil M I, Rafie E, Hebeish A P. Ioninduced grafting of methyl methacrylate onto cotton cellulose\[J\]. Journal of Applied polymer Science, 1981, 26: 149157.
［6］张明杰，许芝. 淀粉接枝系高吸水吸油树脂的合成\[J\]. 化工新型材料, 2007, 35(1): 5960.
［7］曹爱丽, 王强, 张春雪,等. 分散聚合法研制吸水吸油双功能髙聚物\[J\]. 精细化工, 2004, 21(z1): 9093.
［8］王彩旗, 董宇平, 张国,等. 含两亲性PEObPBA增容剂的吸水膨胀橡胶的制备及性能\[J\]. 高分子材料学与工程, 2003,19(4): 200203.
［9］郭双庆, 谢光银. 高吸油吸水性织物的开发及应用\[J\]. 国际纺织导报, 2009, 4: 5556.
［10］Flory P J. Principles of Polymer Chemistry \[M\]. Ithaca: Cornell University Press, 1980:589.

相似文献/References:

备注/Memo

备注/Memo:
收稿日期：20120607作者简介：周爱军（1965），男，湖北武汉人，副教授.研究方向：高分子材料合成与加工.
更新日期/Last Update: