[1]汪艳,周小舟.氢氧化铝及红磷协同阻燃热收缩材料的制备及性能[J].武汉工程大学学报,2012,(11):50-54.[doi:103969/jissn16742869201211011]
　WANG Yan,ZHOU Xiao zhou.Preparation and performance of cooperative flame retardants ofaluminum trihydrate and red phosphorus on heatshrinkable material[J].Journal of Wuhan Institute of Technology,2012,(11):50-54.[doi:103969/jissn16742869201211011]
点击复制


氢氧化铝及红磷协同阻燃热收缩材料的制备及性能(/HTML)
分享到：

《武汉工程大学学报》[ISSN:1674-2869/CN:42-1779/TQ]

卷:
期数:
2012年11期
页码:
50-54
栏目:
资源与土木工程
出版日期:
2012-12-10

文章信息/Info

Title:

Preparation and performance of cooperative flame retardants of
aluminum trihydrate and red phosphorus on heatshrinkable material
文章编号:
16742869(2012)11005005
作者:
汪艳; 周小舟
武汉工程大学材料科学与工程学院，湖北 武汉 430074
Author(s):
WANG Yan;  ZHOU Xiaozhou
School of Material Science and Engineering, Wuhan Institute of Technology, Wuhan 430074,China
关键词:
包覆红磷; 返滴法; 吸水; 机械性能; 热收缩率
Keywords:
encapsulated red phosphorus;  reverse titration;  water absorption;  mechanicalproperties;  heatshrinkable rate
分类号:
TQ324.8
DOI:
103969/jissn16742869201211011
文献标志码:
A
摘要:
采用氢氧化铝（ATH）以及红磷（RP）复配作为阻燃剂，聚乙烯(PE)和乙烯-醋酸乙烯共聚物(EVA)为基体材料，通过化学交联的方法制备新型无卤阻燃热收缩材料.实验结果表明，ATH与RP在分别添加40份和10份的情况下，可以使100份的PE/EVA热收缩材料达到V-0级阻燃；经过ATH沉淀包覆的红磷具有更好的体系相容性，能得到较高的拉伸强度和断裂伸长率；随着EVA份数的增加，热收缩材料的拉伸强度和断裂伸长率随之提高.最佳配方比为PE∶EVA∶ATH∶RP=20∶80∶40∶10.
Abstract:
New halogenfree flame retardant heatshrinkable materials were prepared by chemically cross linking with aluminum trihydrate (ATH) and red phosphorus (RP) compounded as flame retardant, polyethylene (PE) and ethylenevinyl acetate copolymer (EVA) as the basic material. The experimental results indicate that when 40ATH and 10RP respectively are added, the flame retardancy of 100PE/EVA heat shrinkable materials can be achieved to V0. RP precipitated and cladded through ATH has better compatibility, and can get higher tensile strength and breaking elongation. As the addition of EVA, the tensile strength and breaking elongation of heatshrinkable materials are also improved. The best ratio of the formula is PE∶EVA∶ATH∶RP=20∶80∶40∶10.

参考文献/References:

［1］胡晖，张有勇, 申景强，等.国内热收缩材料的研究和产业化的进展\[J\].塑料工业,2007,35(4)：14.
［2］崔隽，姜洪雷,吴明艳，等.阻燃剂的现状与发展趋势\[J\].山东轻工业学院学报，2003，17(1)：1417.
［3］史翎,段雪.阻燃剂的发展及在塑料中的应用\[J\].塑料，2002,31(3)：1115.
［4］叶卫红,刘玲. 红磷/氢氧化镁高效阻燃体系研究\[J\].石化技术与应用，2000,18(6):538540.
［5］鹿海军,马晓燕,颜红侠. 磷系阻燃剂研究新进展\[J\].化工新型材料，2001,29(12)：710.
［6］申云飞,杨贵兰.阻燃剂红磷\[J\].山西化工，1994（1）：2933.
［7］laoutid F, Ferry L, LopezCuesta J M. Red phosphorus/aluminium oxide compositions as flame retardants in recycled poly(ethylene terephthalate)\[J\]. Polymer Degradation and Stability， 2003,82:357363.
［8］曾莉，黄定芳,古星，等. 氢氧化铝中氧化铝含量测定的几种方法比较\[J\].四川理工学院学报，2010,23(5)：583585.

相似文献/References:

备注/Memo

备注/Memo:
收稿日期：20120820作者简介：汪艳（1966），女，湖北武汉人，教授，博士．研究方向：高分子材料配方设计、成型加工、复合改性及快速成型材料等.