溶胶-凝胶模板法制备有序多孔二氧化铈薄膜
(/HTML)
分享到：

《武汉工程大学学报》[ISSN:1674-2869/CN:42-1779/TQ]

卷:
期数:
2012年7期
页码:
29-32
栏目:
资源与土木工程
出版日期:
2012-07-30

文章信息/Info

Title:
Preparation of porous cerium oxide thin film with colloidal crystals
as template
文章编号:
16742869(2012)07002904
作者:
江学良; 杜银;  任军; 吴天骥; 王维
武汉工程大学材料科学与工程学院，湖北 武汉430074
Author(s):
JIANG Xueliang;  DU Ying;  REN Jun;  WU Tianji;  WANG Wei
School of Material Science and Engineering, Wuhan Institute of Technology, Wuhan 430074, China
关键词:
P(St-HEA)微球; 胶体晶体模板法; 二氧化铈; 有序多孔薄膜
Keywords:
P(StHEA) latex particles;  colloidal crystal template;  CeO2;  ordered porous thin film
分类号:
O631
DOI:
103969/jissn16742869201207006
文献标志码:
A
摘要:
采用乳液共聚法制备了聚苯乙烯-丙烯酸羟乙酯\[P(StHEA)\]微球，通过流延成膜法制备了P(StHEA)薄膜，再利用溶胶-凝胶模板法煅烧得到有序多孔二氧化铈（CeO2）薄膜.采用红外光谱、扫描电镜以及X射线衍射分析对P(StHEA)微球单分散性及有序多孔CeO2薄膜表面形貌和结构进行了表征.结果表明，当丙烯酸羟乙酯（HEA）用量占总单体的用量低于10 %(质量分数)时，制备的P(StHEA)微球单分散性和表面较好.通过P(StHEA)的胶体晶体模板制备了有序多孔CeO2薄膜，所得孔径约为190 nm，X射线衍射分析显示有序多孔CeO2薄膜是立方萤石结构.
Abstract:
P(StHEA) latex particles were prepared by emulsion copolymerization. The thin films were obtained by the cast film forming method and a ordered porous cerium oxide (CeO2) thin film was obtained by colloidal crystal templates. The monodispersity of the particles and the structure of ordered porous CeO2 thin film were characterized by infrared spectroscopy, scanning electron microscope and X ray diffraction analysis. The results show that the monodispersity of latex particles and surface quality of colloidal crystal particles are finer at the content of HEA lower than 10%. Ordered porous CeO2 thin films are prepared by the colloidal crystal template, and the average diameter of the porous is about 190 nm. X ray diffraction analysis indicates the porous CeO2 thin film is the facecentered crystal structure.

参考文献/References:

［1］Lou X W, Archer L A, Yang Z C. Hollow micro/nanostructures: synthesis and application \[J\]. Adv Mater, 2008, 20: 1-33.
［2］Ao Y H, Xu J J, Zhang S H, et al. A onepot method to prepare Ndoped titania hollow spheres with high photocatalytic activity under visible light \[J\]. Appl Sur Sci, 2010,256: 2754-2758
［3］Chen C H, Abbas F S, Morey, et al. Controlled synthesis of self-assembled metal oxide hollow spheres via tuning redox potentials: versatile nanostructured cobalt oxides \[J\]. Adv Mater, 2008, 20: 1205-1209.
［4］Wu C Z, Xie Y, Leil Y, et al. Synthesis of new-phased VOOH hollow “dandelions” and their application in lithium-ion batteries \[J\]. Adv Mater, 2006, 18: 1727-1732.
［5］Ma Y R, Qin L M, Ma J M, et al. Facile synthesis of hollow ZnS nanospheres in block copolymer solutions \[J\]. Langmuir, 2003, 19:4040-4042.
［6］Liu Y, Sun D. Development of Fe2O3-CeO2-TiO2/γ-Al2O3 as catalyst for catalytic wet air oxidation of methyl orange azo dye under room condition \[J\]. Appl Catal B, 2007, 72: 205-211.
［7］李海青,闫卫东.聚合物孔材料的合成与应用\[J\]. 高分子通报, 2005(1):25-30.
［8］Guo Z Y, Jian F F, Du F L. A simple method to controlled synthesis of CeO2 hollow microspheres \[J\]. Scr Mater, 2009, 61: 48-51.
［9］秦振平, 郭红霞. 模板法合成有序多孔材料研究进展\[J\]. 化工进展, 2002, 21 (5):323-327.
［10］丁进月， 钟良，赵巧玲.以两亲性共聚物为模板溶胶-凝胶法制备WO3 多孔薄膜及其氢致变色特性的研究\[J\].化学学报，2009，67（2）：179-184.

相似文献/References:

备注/Memo

备注/Memo:
收稿日期：20120316基金项目：湖北省自然科学基金(2011CBD220);湖北省教育厅中青年优秀人才项目（Q20101505）;武汉工程大学研究生教育创新基金项目（20110034）；2012年武汉工程大学大学生校长基金项目作者简介：江学良（1972-），男，安徽肥东人，副教授，博士.研究方向：有机-无机杂化材料与功能高分子.
更新日期/Last Update: